Article

 

Phytosynthesis and Characterization of Silver Nanoparticles Using Leaf Extracts of Premna Serratiffolia L

 

Soumya Soman,  Joseph Ray *

 

Mahatma Gandhi University, School of Biosciences, Kerala 686560 India

 

* Corresponding author:  J. Ray (methikalamray@yahoo.com)

 

Citation: S. Soman and J. Ray. Phytosynthesis and Characterization of silver nanoparticles using leaf extracts of Premna serratiffolia L Nano Biomed. Eng. 2011, 5(4), 155-159.

DOI: 10.5101/nbe.v5i4.p155-159.

 

Abstract

Biosynthesis of nanoparticles using plants and microbes reduce toxicity and enhance biocompatibility of the particles produced. Phytosynthesis makes use of the principle of reduction of metal ions in aquous extracts of plant leaves that may lead to development of nanoparticles. Therefore, production of silver nanoparticles was experimentally tried out using leaf broth of Premna serratifolia L in accordance with standard procedures. The UV-vis spectra gave an SPR band at 422 nm and TEM analysis revealed the formation of nanoparticles in the range of 3-12 nm. The XRD studies showed that particles are crystalline with face centered cube geometry. The reduction and stabilization of the ions are attributed to the hydroxyl and amine groups present in the leaf broth. This method of synthesis of silver nanoparticles has the potential to become an alternative eco-friendly method of synthesis.

 

Keywords: Phytosynthesis, Leaf extract, Phytocompounds, Silver nanoparticles

 

1 Introduction

Nano-biotechnology makes use of nanosized metal particles to have tremendous impact in various medical applications in gene delivery [1-3], in X-Ray imaging [4] and also in nano sensing devices [5]. Physical, chemical and biological methods [6-8] are used to synthesize nanoparticles. Physical and chemical methods are the classic methods, but they are not environment friendly. Harsh solvents or surfactants used in such synthesis generate hazardous waste and uncontrolled release of nanoparticles into environment causing unpredictable consequences to human health and natural biodiversity [9,10]. Therefore, the options of alternative synthesis are seriously experimented. Recently, biosynthesis using plants and microbes is emerging as an eco-friendly method of nanoparticle production. Biosynthesis is a bottom up approach employing biological organisms or materials for  the formation of nanoparticles. Prokaryotic bacteria, actinomycetes and eukaryotic plants are used in reducing metal ions in aquous solutions to metal nanoparticles. Increased tolerance to metals in plants may be an indication of the ability of plant-parts for biosynthesis of nanoparticles [11]. Biosynthesized nanoparticles have many advantages over that of chemically and physically synthesized particles. They are more biocompatible [12] and the synthesis is a single-step protocol [13]. Notable progress has been recorded in phytosynthesis of nanoparticles with controlled size and  shape. Several attempts in  the synthesis of nanoparticles using plant materials such as leaves [14], fruit [15], latex [16] and bark [17] of diverse species are reported. Shankar et al [12] observed that nanoparticles synthesized using plant extracts are stable even after 4-5 weeks of synthesis, attributed the same to diverse kinds of biochemicals present in such plant materials. Among the various nanoparticles, silver nanoparticles have unique applications in diagnostics as biological tags for quantitative detection; and the particles also have conductive and optical applications [18]. Silver particles have antibacterial properties [19] and are used in healthcare and fabrics [20,21]. Plant community is so diverse such that the potential of different plants for synthesis of nanoparticles need to be fully explored. Premna serratifolia L, commonly known as headachetree is a well-known medicinal plant, an ingredient of the famous Ayurvedic ‘dasamola’. The antioxidant properties and tumor cell suppression activities of Premna serratifolia L have been reported [22]. Phytochemicals involved in such properties can not only support and speed up nanoparticle formation, but also can improve biocompatibility of the synthesized nano particles. Therefore, synthesis of silver nanoparticles using the leaf extract of Premna serratifolia L is experimentally tested to examine its potential in nanoparticle synthesis. Synthesis of silver nanoparticles of 3-12 nm and relatively high stability is the success of this attempt.

 

2 Experimental Details

2.1 Plant material and extract preparation

Premna serratifolia L is from the family Verbenaceae. Fresh leaves were collected from Kasargod District of Kerala State. About 10 g of the fresh leaves were initially surface cleaned with the detergent Tween 20, then in running tap water and finally in ultrapure water . Leaves were cut into small pieces and the chopped leaves were boiled in 75 mL ultrapure water for 5 mts in a 500 mL Erlenmeyer flask. The plant extract obtained was allowed to cool. It was then decanted and filtered using Whatmann No.1 paper. The color of the broth was noted and stored in refrigerator at 4oC for future use. The plant extract was used within seven days for synthesis of nanoparticles.

 

2.2 Phytosynthesis of silver nanoparticles

Silver nitrate was obtained from HiMedia. For understanding the impact of concentration of Silver Nitrate on synthesis of nanoparticles, reaction mixtures of 1 ml leaf broth and 1 mM  silver nitrate solution in the ratios of 1:10, 1:20, 1:30, 1:40, 1:50 (named as S1- S5) were tried in triplicates. Pure 1 mM Silver nitrate solution and the plant extract were kept as control. All the experimental trials and controls were kept in darkness at room temperature for 48 hours. Monitoring of the changes in experimental trials was carried out from 45 minutes onwards.

After four to 6 hours, part of this reaction mixture was used for UV-vis analysis. The rest of the reaction mixtures after forty eight hours was subjected to FTIR characterization and afterwards were centrifuged at 10,000 rpm for 10 mts [23] and the pellet obtained was used for TEM, XRD, EDS characterization. The pellets were washed 2-3 times to remove impurities and resuspended in ultrapure water before characterization.

 

2.3 UV-vis spectral and TEM analysis

The reaction mixture was diluted to 10−1 and the reduction was observed through UV-Vis spectrophoto- meter (Thermoscientific) with a resolution of 1nm, between 200 to 1100 nm. The TEM images (JEOL-TEM) were used to estimate the particle size. A thin film of the nanoparticles extracted from the reaction mixture as pellets was coated on to carbon coated-copper grid [24].

 

2.4 XRD & EDS

The crystalline nature of Ag nanoparticles was further confirmed from X-ray diffraction (PANanalytical Powder XRD instrument) analysis. Nanoparticles obtained were made into a thin film and analyzed [24]. The presence of elemental silver was examined using EDS (JEOL- JSM 6390 SEM) instrument.

 

2.5 FTIR studies

These studies were carried out using Shimadzu FTIR spectrometer in attenuated total reflection mode and using an range of 4000-400 cm−1  and resolution of 4 cm−1.

 

3 Results and Discussion

3.1 Phytosynthesis of silver nanoparticles

Change in intensity of color of the reaction mixture was taken as the preliminary evidence of nanoparticle synthesis. A color change of the reaction mixture was observed from transparent yellow to reddish brown within 45 mts at room temperature. The appearance of reddish brown color from excitation of surface plasmon vibrations of silver nanoparticles is a clear indication of the formation of Ag nanoparticles [25,26]. There was no color change in any sample of the reaction mixture after 4 to 6 hrs and the same remained stable up to seven months.

 

3.2 UV-vis  spectral analysis

Among the five reaction mixtures, S1 to S5, an SPR peak is seen in all the five, but S1 showed a broad peak compared to that obtained in S2. Then in S3 to S5, along with SPR, peaks of silver nitrate were also obtained. Therefore, the reaction mixture S2 (1:20) was selected for further study as it showed an optimum absorbance compared to others. Fig. 1 shows the results obtained in UV-vis spectra of plant extract (a), silver nitrate (b) and S2 reaction mixture (c), taken after 6 h of incubation. A fairly sharp and symmetrical Surface Plasmon Resonance (SPR) peak obtained for S2 is indicative of small spherical particles. The broad centered peak obtained at 422 nm indicates slow reduction of silver ions to siver nanoparticles [27]. Appearance of silmilar peak, assigned to  surface plasmon, have been documneted by  Anwad et al [26] at 425 nm and Krishnaraj et al at 420 nm [28]. Electrons on the metal surface undergo collective oscillation when excited by light at specific wavelength, which is known as SPR. This oscillation results in unusually strong scattering and absorption properties and the absorbance is measured using UV-Vis Spectroscopy, there by analysing the reduction of silver ions [29].

 

3.3 TEM analysis

Typical TEM images obtained with colloid S2 after 48 h are shown in Fig. 2 (a to d). At low magnification, large numbers of silver nanoparticles are seen. Thus the nanoparticles are quite mono dispersed and ranged in size from 3-12 nm with an average of 4 nm.The morphology of nanoparticles are clearly seen at higher magnification and mainly they are spherical. This result is in agreement with the shape of the SPR band obtained at 422 nm, as is seen in Fig.1. In Fig. 2e the particle size distribution histogram of nano-particles obtained from HRTEM image is shown. Close examina- tion of the TEM images showed that there is no physical contact between the particles. Moreover, a material coating is visible on the particles (Fig. 2a and 2b), which may be attributed bio organic components of the leaf broth as a covering on the nanoparticles. Shankar et al [30] have recorded similar observations on nanoparticles synthesized using geranium leaf extracts. The TEM analysis shows the size and morphology of the synthesized nanoparticles. The high resolution TEM image of a single nanoparticle in Fig. 2c, which shows good crystallinity of the silver nanoparticles. The distance of 0.23 nm between the lattice planes is in agreement with the (111) lattice spacing of face centered cubic (fcc) silver (d111=0.2359 nm). Similar results have been reported by Philip et al [27] and Dubey et al [31]. The selected area diffraction pattern (SAED) of the Ag nanoparticles is  shown in  Fig. 2d.  Further the  ring like diffraction pattern indicates that the particles are crystalline [24]. Average particle size was calculated to be 4.1 nm from the histogram obtained.

 

3.4 XRD &EDX analysis

The X ray diffraction confirmed the crystalline nature of silver nanoparticles. Fig 3 shows the XRD pattern obtained for silver nanoparticles synthesized using the Premna serratifolia L leaf broth. The three diffraction peaks observed in the 2 theta range 30-70 can be indexed to the (111), (200), (220) planes of fcc silver (JCPDS file no.04-0783) [27,32]. The (200), (220) Bragg reflections are weak relative to the intense (111) reflection [33]. This feature indicates that the Nano crystals are (111) oriented as confirmed by TEM measurements [34]. Fig 4 shows the preliminary EDS measurements carried out using the JEOL-JSM 6390 SEM instrument. An intense optical absorption band peak was observed at 3 KeV, [35] which is typical of the absorption of metallic Ag Nano particles due to SPR. This further confirms the formation of silver nanoparticles by Premna  serratifolia L leaf broth on  exposure to  silver nitrate.These results are consistent with Vanaja et al [36], where silver nanoparticles have been synthesized using leaf extracts of Coleus aromaticus.

 

3.5 FTIR studies

Fig. 5 shows the FT-IR spectra of capped silver nano- particles using Premna serratifolia L leaf broth. FTIR is done to identify the potential biomolecules responsible for reduction and capping of the bioreduced metal nanoparticles. In Fig. 5, the IR spectrum of silver nanoparticles gives prominent bands at 3334, 3319, 3298 and 3265 cm−1 which indicates the –OH stretching [38] and medium peaks between 1330 and 1450 cm−1 is due to – OH bending and both this accounts for the presence of secondary alcohols and phenols [37]. A strong IR signal at 1636 cm−1 corresponds –C=C stretching vibration [38]. Peaks at 1456, 1473 and 1489 cm−1 corresponds to the –C– C asymmetric bending [37]. The peaks at 2980 cm−1 indicates –CH stretching and peaks at 1381 cm−1, 943 cm−1 give –CH bending vibrations which may be due to –CH3 and –CH2 functional groups. At 1251 cm−1 there is a broad peak which may be due to –C–O stretch alcohols and phenols. The series of peaks between 1250-1012 cm−1 corresponds to –CN stretching of aliphatic amines. The peaks between 1020 and 1091 cm−1 correspond to alcohols or phenols. The presence of amines or alcohols or phenols represents the presence of polyphenols which may be flavonoids. Similar results have been reported by Vanaja et al [36]. The study on the phytochemical analysis of Premna serratifolia L [39] shows the presence of flavanoids, terpenoids, phenolic compounds,sugars and proteins. The vibrational bands corresponding to the bonds such as –C=C–, –CO and –C–O–C– are derived from water soluble compounds such as flavonoids, alkaloids present in the Premna serratifolia L, Thus the FTIR data indicate the presence of alcohols,aliphatic amines and phenolic compounds present in the leaf broth. It is certainly possible that these bio molecules act as reducing agents and may be responsible for mediating synthesis, capping and stabilization. Especially the amine and   hydroxyl groups present in the leaf extract of Premna serratifolia L broth might be having a positive role in the reduction and capping of silver nanoparticles.

 

 

Fig. 1 V-vis Spectra of (a)plant extract,(b)silver nitrate,(c)Reaction mixture S2

 

Fig. 2 TEM analysis and Particle size Histogram of Silver nanoparticles.

 

Fig. 3 XRD pattern of silver nanoparticles synthesized using Premna serratifolia leaf broth.

 

Fig. 4 Energy Dispersive X ray absorption spectroscopy.

 

Fig. 5 FT-IR spetrum of silver nanoparticles synthesized by Premna leaves broth.

 

4 Conclusions

The influence of leaf broth of Premna serratifolia L on silver nitrate have been shown and a 1:20 reaction mixture of leaf broth and 1 mM Silver Nitrate solution was found to be the best combination compared to the other ratios analysed for nanoparticle synthesis. The size of nanoparticles produced ranged from 3-12 nm. In general, phytosynthesized nanoparticles are considered to be environmentally benign having applications in food, agriculture, medicine and cosmetics. Therefore, the current observations of eco friendly synthesis of silver nanoparticles using leaf broth of a medicinal tree, Premna serratifolia L has high relevance. Especially, the newly synthesized particles are found to be quite stable and no visible changes were observed even after seven months. There were no change in the UV-vis spectroscopy values even without the addition of any stabilizing agents during this period of observaion. The reduction and stabilization of silver nanoparticles is believed to be by phenolic compounds present in the leaf broth of Premna serratifolia L. But the exact mechanism of formation and how the biomolecules interact with particles have to be further looked into. In order to make this kind of synthesis as a viable and alternative method to chemical synthesis, large scale production under controlled environmental conditions such as temperature, pH, concentration of silver nitrate and the like should be standardized. Experiments for the same are being checked in the laboratory.

 

Acknowledgements

Instrumentation facilities provided by IIRBS, MGU for UV Vis spectroscopy, School of Chemical Sciences for EDS analysis, DBT MSUB facilities at School of Biosciences for FTIR studies, Centre of nanoscience at Mahatma Gandhi University for TEM are gratefully acknowledged.

 

References

 

Copyright:(c) 2013 S. Soman and J. Ray. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.